English translation for "reaction order"

反应次序
反应级数

Example Sentences:

	1.	3 . kinetic study of phase change of the composite materials was given by dsc method , the activation energies and the reaction orders of the phase changes in the composite materials were calculated 3 、运用dsc对上述复合贮能材料的相变动力学进行了研究，确定了各相变过程的表观活化能值及反应级数。
	2.	The reaction order and apparent activation energy of nanocomposites by emulsion and bulk methods are obviously increased . this also shows that the thermal stability of nanocomposites is much better than pure pmma , which is also confirmed by doyle method Freeman - carroll差减微分法结果表明：本体法及乳液法复合材料的热分解反应级数和表观活化能均明显高于纯pmma ； doyle积分法佐证了这一点。
	3.	The first peak was analyzed by the doyle equation , it found that the apparent decomposition reaction order was 1 . 0 both of in n2 and in air . the decomposition activation energy was lower in n2 than of in air , which was 147 . 405 kj - mol - 1 and 192 . 656kj 采用doyle方程对第一个峰进行数学分析，发现其热分解过程满足一级反应方程式，在氮气气氛中的分解活化能小于在空气中的活化能，分别为147 . 405kj
	4.	The thermal decompostion kinetics of up / montmorillonite nanocomposites under nitrogen was studied . the reaction order and apparent activation energy of nanocomposites were obtained by freeman - carroll method . the results indicate the thermal stability of nanocomposites is higher than pure up ' s 研究了氮气气氛下不饱和聚酯蒙脱土纳米复合材料的热分解动力学，用freeman - carroll法确定了复合材料的反应级数n和表观反应活化能e 。
	5.	Poly - o - toluidine ( pot ) is selected as the electro - catalyst of 2 , 5 - dimercaptan - 1 , 3 , 4 - thiadiazole ( dmct ) because the solubility of pot in organic solvents is much higher than that of pan . therefore , dmct can contact with pot at molecular level . it suggests that the oxidative reaction order is 2 and the reduced reaction order is 1 by testing its electrode kinetics 聚苯胺难以溶于有机溶剂,因此选用易溶于有机溶剂的聚苯胺衍生物聚邻甲基苯胺( pot )作有机硫化合物2 , 5 -二巯基- 1 , 3 , 4 -噻二唑( dmct )的电催化剂,两者可以达到分子水平的复合。
	6.	The curing kinetics parameters of up with lwt % organic montmorillonite were determined by the dynamic dsc . its apparent activation energy is higher than pure up ' s , but reaction order is similar . these results show the addition of organic montmorillonite increase difficulty degree of curing reaction 采用非等温dsc法计算出的含有机蒙脱土1wt的不饱和聚酯树脂的表观反应活化能和固化温度高于不饱和聚酯树脂，但反应级数基本没有变化，说明加入有机蒙脱土使树脂的固化反应难度增大。
	7.	( 2 ) xrd analysis showed that phenolic resin molecules could insert into the interlayer of organic - montmorillonite , but there are some differences of the behavior of intercalation between thermosetting phenolic resin and thermoplastic phenolic resin . ( 3 ) the cure kinetics parameters of epoxy resin / org - mmt / deta , epoxy resin / org - mmt / toa and epoxy resin / org - mmt / mz nanocomposites were investigated by differential scanning calorimetry ( dsc ) . some kinetics parameters including the reaction order and activation energy were caculated with kissinger method ( 3 ) dsc研究了环氧树脂二乙烯三胺蒙脱土、环氧树脂桐油酸酐蒙脱土、环氧树脂咪唑蒙脱土固化体系在不同org - mmt配比( 0 ， 5 ， 10 )及不同温度下的固化动力学，除了运用常见的kissinger和crane方法求出活化能和反应级数等动力学参数外，还尝试了用修正的avrami方程和自催化动力学模型研究了环氧树脂蒙脱土体系的固化动力学。
	8.	As to epoxy / toa / org - mmt system , the reaction order was 0 . 9 and active energy was 66kj / mol by kissinger method ; and a similar result was obtained by ozawa method . the curing reaction was controlled clearly by diffusion mechanism in the later stage of curing reaction without addition of org - mmt , which leads to the increment of active energy with extend of curing ; as to the curing system with addition of org - mmt , the value of active energy was always kept the same level , which can be explained by the catalytic function of amine salt inserted in the galleries of org - mmt 对于环氧桐油酸酐有机蒙脱土固化体系用kissinger方法看到固化体系的反应级数均为0 . 9左右，表观活化能值为66kj mol ； ozawa方法的处理结果与之近似，但从ozawa方法可以看到未加入有机蒙脱土的体系在反应后期固化反应明显受扩散控制，表现为活化能随固化程度的增加而增加；而加入有机蒙脱土的体系，其表观活化能则自始至终表现的较为均匀。

Similar Words：

"reaction of the second order" English translation, "reaction of the su ort" English translation, "reaction of the support" English translation, "reaction of total degeneration" English translation, "reaction oil" English translation, "reaction ore" English translation, "reaction overpotential" English translation, "reaction pad" English translation, "reaction pair" English translation, "reaction paper" English translation